Product Introduction:
17003 is a modified acrylic adhesive cured by ultraviolet and visible light, specifically developed for the bonding, fixation, and sealing of electronic components and parts in medical equipment. It has the characteristics of good adhesion, flexibility, strong earthquake resistance, and good weather resistance. It has the advantages of fast deep curing and good surface drying.
Product performance before curing:
| Appearance |
Slightly yellow or transparent liquid |
|
| ViscosityCPS |
9000±500 |
Brookfield DV-Ⅱviscometer，25℃，SC 4-15/150rpm |
| hardness(Shao D)) |
55-70 |
GB/T2411-1980Curing test |
| elongation at break％ |
300-400 |
GB/T528-1998Curing test |
Curing conditions:
17003 will cure under ultraviolet light and also slowly cure under sunlight. The curing rate, final curing depth, and surface drying effect are related to factors such as UV light source, illumination time, and material transmittance. Suggest determining the specific curing time through experimentation.
Positioning time:
2mm thick ordinary glass:
10 seconds - F20T8 BL UV lamp tube; 6-second-125W PHILIPS high-pressure fluorescent lamp
Fully Curding Time:
240 seconds - F20T8 BL ultraviolet lamp tube; 180 seconds -125W PHILIPS high-pressure fluorescent lamp
Electrical performance：
| Thermal expansion coefficient |
80×10 |
| Thermal conductivity coefficient W/(m · K) |
0.1 |
| Volume resistivityΩ·cm |
2×10 |
| dielectric constant/Dielectric loss |
|
| 100Hz |
5.3/0.03 |
Product performance after curing:
| Hardness (Shore D) |
68 |
(GB/T 2411-1980) |
| Light transmittance |
88-95 |
|
| Shrinkage rate |
3.8-6.0 |
|
Tensile and shear strength (GB 7124-86), overlap area of approximately 25 × 12=300mm
Stainless steel bonded glass
The glass sheet is bonded to a 3mm thick stainless steel plate as a test piece at a temperature of 25 ℃
Tensile and shear strength ≥ 10MPa, glass damage;
Instructions and Precautions:
1、 The bonding surface should be kept clean, dry, and free of grease. It can be wiped with acetone or dried with a hair dryer.
2、 UV lamp irradiation positioning curing, the curing rate depends on the light energy absorbed by the adhesive solution, and is related to factors such as the distance from the light source and the transmittance of the material.
3、 During operation, excessive force should not be applied to squeeze the adhered object, and it is not allowed to repeatedly move or separate the adhered object.
4、 Do not pour the remaining glue back into the original packaging to avoid contamination.
5、 The glue after opening should be used up within a week.
6、 This product has slight irritation to the eyes and skin. If accidentally splashed into the eyes, rinse immediately with plenty of water. If discomfort persists, seek medical examination. Please rinse immediately with soapy water after skin contact. Please wash the clothes before wearing them.
Storage conditions and packaging specifications:
Please store in a cool and dark place, with the best storage temperature between 10-25 ℃ and a shelf life of 6 months.
1KG per bottle or packaging provided according to customer requirements.
Explanation: The various data contained in this article were measured by Dingxin technicians in the laboratory and have certain reference value for customers' use. However, due to the different usage methods and conditions of each customer, it is recommended that customers find the best process and method based on their own situation. If you have any questions or would like to learn more, please feel free to call 15920255718 for consultation.